Yumuşak astar ve PMMA arasındaki çekme bağlantı dayanımına ozon gaz etkisi
Öz
Objectives: To investigate the effects of application of ozone with different durations on the bond strength between PMMA and soft liner material
Materials and Methods: The soft liner tested in this study was a heat processed silicone-based material, Molloplast B (ML) (Detax, Ettlingen, Germany), and the denture base material was a heat-cured poly (methyl methacrylate) (PMMA) acrylic resin material (Meliodent, Bayer Dental, Newbury, UK). Four sample groups were formed and each of them consisted of 5 specimens. Groups of 2, 3, and 4 were performed ozone gaseous 40, 80,120 s respectively. But not group 1
Results: Group 4 revealed the lowest strength 28.60±1.51, being statistically different from those of the specimens in the other groups (p<0.05).
Conclusions: Group 1 (untreatment ozone gaseous) offered the best tensile bond strength 40.40±3.50 values among the tested groups. As increasing ozone treatment duration to PMMA surface, decreasing tensile bond strength of sample groups.
ÖZET
Amaç: Farklı sürelerde ozon uygulanan PMMA yüzeylerinin yumuşak astar materyali ile yaptığı bağlantı dayanımına etkisini araştırmakdır.
Gereç ve Yöntem: Bu çalışmada yumuşak astar materyali olan Molloplast-B (Detax, Ettlingen, Germany) ve protez kaide materyali ısıyla polimerize edilen PMMA (Meliodent, Bayer Dental, Newbury, UK) akrilik rezin kullanıldı. 4 örnek grubu ve her bir grup için 5 örnek hazırlandı. Grup 2, 3 ve 4 örnek gruplarına sırasıyla 40, 80, 120 sn ozon gazı uygulaması yapıldı. Grup 1 kontrol grubu olarak değerlendirildi.
Bulgular: 120 sn ozon uygulanan grup 4 en düşük bağlantı dayanım 28,60±1,51değerine sahiptir. Ve diğer gruplar arasında farklılık önemli bulunmuştur (p<0,05).
Sonuç: Test grupları arasında Ozon gazı uygulanmayan grup 1 en yüksek bağlantı dayanım 40.40±3.50değerine sahiptir. PMMA yüzeylerine ozon uygulama süresi arttıkça örnek grupların bağlantı dayanım değerlerinde düşüş olduğu görüldü.
Anahtar Kelimeler
References
- Kaynaklar
- Hayakawa I, Keh E, Morizawa M, Muraoka G, Hirano S. A new polyisoprene-based light-curing denture soft lining material. J Dentistry 2003; 31: 269-274.
- Anusavice KJ, Phillip’s Science of Dental Materials, (W.B. Saunders Co., Philadelphia, PA, USA, 1996), 10th ed., pp. 264–265.
- Pinto JRR, Mesquita MF, Nobilo MAA, and Henriques GEP. Evaluation of varying amounts of thermal cycling on bond strength and permanent deformation of two resilient denture liners. J Prosthet Dent 2004; 92: 288–293.
- Sinobad D, Murphy WM, Huggett R, and Brooks S. Bond strength and rupture properties of some soft denture liners. J Oral Rehabil 1992; 19: 151–160.
- Minami H, Suzuki S, Ohashi H, Kurashige H, Tanaka T. Effect of surface treatment on the bonding of an autopolymerizing soft denture liner to a denture base resin. Int J Prosthodont 2004; 17: 297–301.
- Waters MGJ, Jagger RG. Mechanical properties of an experimental denture soft lining material. J Dent 1999; 27: 197-202.
- Emmer TJJr, Emmer TJSr. Bond strength of permanent soft denture liners bonded to the denture base. J Prosthet Dent 1995; 74: 595-601.
Details
Primary Language
Turkish
Subjects
-
Journal Section
-
Publication Date
August 6, 2014
Submission Date
September 28, 2013
Acceptance Date
-
Published in Issue
Year 2014 Volume: 17 Number: 3
Cited By
Wettability of polymer materials with different liquids and effect of contact angle test liquids on calculated surface free energy value
Journal of Dispersion Science and Technology
https://doi.org/10.1080/01932691.2024.2440417