Abstract
Objectives: The aim of this study was to assess the effects direct or indirect water exposure on the 3 months hydrolytic degradation of three dentin bonding agents.
Materials and methods: The samples were divided in three groups: Clearfil SE Bond, Clearfil S3, Adper Singlebond 2; and the samples were restored with Filtek Z350. Subsequent to the restorative procedures, the specimens of each group were divided into three subgroups (immersed in water deionised): Control (24h-37ºC), Direct Water exposure DWE for 3 months (37º), Indirect water exposure (IWE-3m) with enamel margins for 3 months (37ºC). After the storage the samples were sectioned into sticks and µTBS testing (EZ test) and Scanning Electronic Microscopy assessed the failure mode. The µTBS data were statistically analysed using two-way ANOVA and Tukey’s test at α=0.05%. The samples were processed for nanoleakage evaluation immersed in 50 wt% ammoniacal silver nitrate (24 h), rinsed and immersed in a photo-developing solution for 8 h.
Results: After 3 months CSE was the least affected by water degradation regardless the aging strategy. IWE afforded very little variation on µTBS after 3 m. Intense nanoleakage was observed with DWE groups with increases incidence of mixed failures instead
Conclusion: Bonded dentin margins are more prone to hydrolytic degradation than resin-enamel interfaces. The increased nanoleakage and the drop of bond strength showed this.
References
- Reis AF, Giannini M, Pereira PN. Effects of a peripheral enamel bond on the long-term effectiveness of dentin bonding agents exposed to water in vitro. J Biomed Mater Res Part B: Applied Biomaterials 2008;85:10-17
- Feitosa VP, Correr AB, CorrerSobrinho L, Sinhoreti MA. Effect of a new method to simulate pulpal pressure on bond strength and nanoleakage of dental adhesives to dentin. J Adhes Dent 2012;14:5175
- Tjäderhane L, Nascimento FD, Breschi L, Mazzoni A, Tersariol IL, Geraldi S, Tezvergil-Mutluay A, Carrilho MR, Carvalho RM, Tay FR, Pashley DH. Optimizing dentin bond durability: control of collagen degradation by matrix metalloproteinases and cysteine cathepsins. Dent Mater 2013;29:116135
- De Munck J, Van Meerbeek B, Yoshida Y, Inoue S, Vargas M, Suzuki K, Lambrechts P, Vanherle G. Four-year water degradation of total-etch adhesives bonded to dentin. J Dent Res 2003;82:136-140. Van Landuyt KL, De Munck J, Mine A, Cardoso MV, Peumans M, Van Meerbeek B. Filler debonding & subhybrid-layer failures in self-etch adhesives. J Dent Res 2010;89:104510
- Tay FR, Pashley DH, Yoshiyama M. Two modes of nanoleakage expression in single-step adhesives. J Dent Res 2002;81:472-476.
- Van Landuyt KL, Yoshida Y, Hirata I, Snauwaert J, De Munck J, Okasaki M, Suzuki K, Lambrechts P, Van Meerbeek B. Influence of the chemical structure of functional monomers on their adhesive performance. J Dent Res 2008;87:757-761.
- Loguercio AD, Reis A. application of a dental adhesive using the selfetch and etch-and-rinse approaches: an 18-month clinical evaluation. JADA 2008;139:53-61.
- Bracket WW, Ito S, Tay FR, Haisch LD, Pashley D. Micro tensile bond strength of self-etching resin: effect of a hydrophobic layer. Oper Dent 2005;30:733-738.
- Sauro S, Manocci F, Toledano M, Osorio R Thompson I, Watson TF. Influence of hydrostatic pulpal pressure on droplets formation in current etch-and-rinse and self-etch adhesives: a video rate/TSM microscopy and fluid filtration study Dent Mater 2009;25:1392-1402.
- Sauro S, Pashley DH, Montanari M, Chersoni S, Carvalho RM, Toledano M, Osorio R, Tay FR, Prati C. Effect of simulated pulpal pressure on dentin permeability and adhesion of self-etch adhesives. Dent Mater 2007;23:705-713.
- Feitosa VP, Sauro S, Watson TF, Correr AB, Osorio R, Toledano M, Correr-Sobrinho L, Sinhoreti MA. Evaluation of the micro-mechanical strength of resin bonded-dentin interfaces submitted to short-term degradation strategies. J Mechanic Behav Biomed Mater 2012;15:112
- Tay FR, Pashley DH, Yoshiyama M. Two modes of nanoleakage expression in single-step adhesives. J Dent Res 2002;81:472-476.
- Feitosa VP, Leme AA, Sauro S, Correr-Sobrinho L, Watson TF, Sinhoreti MA, Correr AB. Hydrolytic degradation of the resindentine interface induced by the simulated pulpal pressure, direct and indirect water ageing. J Dent 2012;40:1134-1143.
- Scaffa P.M.C, Vidal C.M.P, Barros N, Gesteira T.F, Carmona A.K, Breschi L, Pashley D.H, Tjäderhane L, Tersariol I.L.S, Nascimento F.D, Carrilho M.R. Chlorhexidine inhibits the activity of dental cysteine cathepsins 2012 J Dent Res 2012;91:420-425.
- Hashimoto M, Fujita S, Nagano F, Ohno H, Endo K. Ten-years degradation of resin-dentin bonds. Eur J Oral Sci 2010;118:404-410.
- Liu Y, Van Meerbeek B, Yoshida Y, Inoue S, Vargas M, Suzuki K, Lambrechts P, Vanherle G. Limitation in Bonding to dentin and experimental Strategies to prevent bond degradation J Dent Res 2011;90:953-968.
- Mazzoni A, Scaffa P, Carrilho M, Tjäderhane L, Di Lenarda R, Polimeni A, Tezvergil-Mutluay A, Tay FR, Pahley DH, Breschi L. Effects of etch-and-rinse and selfetch adhesives on dentin MMP-2 and MMP- J Dent Res 2013;92:82-86.
- Skovron L, Kogeo D, Gordillo LA, Meier MM, Gomes OM, Reis A, Loguercio AD. Effects of immersion time and frequency of water exchange on durability of etch-andrinse adhesive. J Biomed Mater Res Part B: Applied Biomaterials 2010;95:339-346.
- Toledano M, Osorio R, Osorio E, Aguilera FS, Yamauti M, Pashley DH, Tar F. Durability of resin-dentin bonds: effects of direct/indirect exposure and storage media. Dent Mater 2007;23:885-892.
- Tay FR, Hashimoto M, Pashley DH, Peters MC, Lai SCN, Yiu CKY, Cheong C. Aging affects two modes of nanoleakage expression in bonded dentin. J Dent Res 2003;82:537-541.
- Torkabadi S, Nakajima M, Ikeda M, Foxton RM, Tagami J. Influence of bonded enamel margins on dentin bonding stability of one-step selfetching adhesives. J Adhes Dent 2009;11:347-353.
- Hosaka K, Masatoshi N, Monticelli F, Carrilho M, Yamauti M, Aksornmuang J, Nishitani Y, Tay FR, Pashley DH, Tagami J. Influence of hydrostatic pulpal pressure on the microtensile bond strength of all-inone self-etching adhesives. J Adhes Dent 2007;9:437-442.
Abstract
References
- Reis AF, Giannini M, Pereira PN. Effects of a peripheral enamel bond on the long-term effectiveness of dentin bonding agents exposed to water in vitro. J Biomed Mater Res Part B: Applied Biomaterials 2008;85:10-17
- Feitosa VP, Correr AB, CorrerSobrinho L, Sinhoreti MA. Effect of a new method to simulate pulpal pressure on bond strength and nanoleakage of dental adhesives to dentin. J Adhes Dent 2012;14:5175
- Tjäderhane L, Nascimento FD, Breschi L, Mazzoni A, Tersariol IL, Geraldi S, Tezvergil-Mutluay A, Carrilho MR, Carvalho RM, Tay FR, Pashley DH. Optimizing dentin bond durability: control of collagen degradation by matrix metalloproteinases and cysteine cathepsins. Dent Mater 2013;29:116135
- De Munck J, Van Meerbeek B, Yoshida Y, Inoue S, Vargas M, Suzuki K, Lambrechts P, Vanherle G. Four-year water degradation of total-etch adhesives bonded to dentin. J Dent Res 2003;82:136-140. Van Landuyt KL, De Munck J, Mine A, Cardoso MV, Peumans M, Van Meerbeek B. Filler debonding & subhybrid-layer failures in self-etch adhesives. J Dent Res 2010;89:104510
- Tay FR, Pashley DH, Yoshiyama M. Two modes of nanoleakage expression in single-step adhesives. J Dent Res 2002;81:472-476.
- Van Landuyt KL, Yoshida Y, Hirata I, Snauwaert J, De Munck J, Okasaki M, Suzuki K, Lambrechts P, Van Meerbeek B. Influence of the chemical structure of functional monomers on their adhesive performance. J Dent Res 2008;87:757-761.
- Loguercio AD, Reis A. application of a dental adhesive using the selfetch and etch-and-rinse approaches: an 18-month clinical evaluation. JADA 2008;139:53-61.
- Bracket WW, Ito S, Tay FR, Haisch LD, Pashley D. Micro tensile bond strength of self-etching resin: effect of a hydrophobic layer. Oper Dent 2005;30:733-738.
- Sauro S, Manocci F, Toledano M, Osorio R Thompson I, Watson TF. Influence of hydrostatic pulpal pressure on droplets formation in current etch-and-rinse and self-etch adhesives: a video rate/TSM microscopy and fluid filtration study Dent Mater 2009;25:1392-1402.
- Sauro S, Pashley DH, Montanari M, Chersoni S, Carvalho RM, Toledano M, Osorio R, Tay FR, Prati C. Effect of simulated pulpal pressure on dentin permeability and adhesion of self-etch adhesives. Dent Mater 2007;23:705-713.
- Feitosa VP, Sauro S, Watson TF, Correr AB, Osorio R, Toledano M, Correr-Sobrinho L, Sinhoreti MA. Evaluation of the micro-mechanical strength of resin bonded-dentin interfaces submitted to short-term degradation strategies. J Mechanic Behav Biomed Mater 2012;15:112
- Tay FR, Pashley DH, Yoshiyama M. Two modes of nanoleakage expression in single-step adhesives. J Dent Res 2002;81:472-476.
- Feitosa VP, Leme AA, Sauro S, Correr-Sobrinho L, Watson TF, Sinhoreti MA, Correr AB. Hydrolytic degradation of the resindentine interface induced by the simulated pulpal pressure, direct and indirect water ageing. J Dent 2012;40:1134-1143.
- Scaffa P.M.C, Vidal C.M.P, Barros N, Gesteira T.F, Carmona A.K, Breschi L, Pashley D.H, Tjäderhane L, Tersariol I.L.S, Nascimento F.D, Carrilho M.R. Chlorhexidine inhibits the activity of dental cysteine cathepsins 2012 J Dent Res 2012;91:420-425.
- Hashimoto M, Fujita S, Nagano F, Ohno H, Endo K. Ten-years degradation of resin-dentin bonds. Eur J Oral Sci 2010;118:404-410.
- Liu Y, Van Meerbeek B, Yoshida Y, Inoue S, Vargas M, Suzuki K, Lambrechts P, Vanherle G. Limitation in Bonding to dentin and experimental Strategies to prevent bond degradation J Dent Res 2011;90:953-968.
- Mazzoni A, Scaffa P, Carrilho M, Tjäderhane L, Di Lenarda R, Polimeni A, Tezvergil-Mutluay A, Tay FR, Pahley DH, Breschi L. Effects of etch-and-rinse and selfetch adhesives on dentin MMP-2 and MMP- J Dent Res 2013;92:82-86.
- Skovron L, Kogeo D, Gordillo LA, Meier MM, Gomes OM, Reis A, Loguercio AD. Effects of immersion time and frequency of water exchange on durability of etch-andrinse adhesive. J Biomed Mater Res Part B: Applied Biomaterials 2010;95:339-346.
- Toledano M, Osorio R, Osorio E, Aguilera FS, Yamauti M, Pashley DH, Tar F. Durability of resin-dentin bonds: effects of direct/indirect exposure and storage media. Dent Mater 2007;23:885-892.
- Tay FR, Hashimoto M, Pashley DH, Peters MC, Lai SCN, Yiu CKY, Cheong C. Aging affects two modes of nanoleakage expression in bonded dentin. J Dent Res 2003;82:537-541.
- Torkabadi S, Nakajima M, Ikeda M, Foxton RM, Tagami J. Influence of bonded enamel margins on dentin bonding stability of one-step selfetching adhesives. J Adhes Dent 2009;11:347-353.
- Hosaka K, Masatoshi N, Monticelli F, Carrilho M, Yamauti M, Aksornmuang J, Nishitani Y, Tay FR, Pashley DH, Tagami J. Influence of hydrostatic pulpal pressure on the microtensile bond strength of all-inone self-etching adhesives. J Adhes Dent 2007;9:437-442.
Details
| Primary Language | English |
|---|---|
| Journal Section | Original Research Articles |
| Authors | |
| Publication Date | January 24, 2014 |
| Submission Date | May 10, 2013 |
| Published in Issue | Year 2014Volume: 17 Issue: 1 |
Cumhuriyet Dental Journal (Cumhuriyet Dent J, CDJ) is the official publication of Cumhuriyet University Faculty of Dentistry. CDJ is an international journal dedicated to the latest advancement of dentistry. The aim of this journal is to provide a platform for scientists and academicians all over the world to promote, share, and discuss various new issues and developments in different areas of dentistry. First issue of the Journal of Cumhuriyet University Faculty of Dentistry was published in 1998. In 2010, journal's name was changed as Cumhuriyet Dental Journal. Journal’s publication language is English.
CDJ accepts articles in English. Submitting a paper to CDJ is free of charges. In addition, CDJ has not have article processing charges.
Frequency: Four times a year (March, June, September, and December)
IMPORTANT NOTICE
All users of Cumhuriyet Dental Journal should visit to their user's home page through the "https://dergipark.org.tr/tr/user" " or "https://dergipark.org.tr/en/user" links to update their incomplete information shown in blue or yellow warnings and update their e-mail addresses and information to the DergiPark system. Otherwise, the e-mails from the journal will not be seen or fall into the SPAM folder. Please fill in all missing part in the relevant field.
Please visit journal's AUTHOR GUIDELINE to see revised policy and submission rules to be held since 2020.