Yorulma testinin, üç farklı tam seramik yapım sistemi vertikal kırılma Direnci üzerine etkisi

Year 2009, Volume: 12 Issue: 1, 16 - 21, 01.11.2011

Abstract

Purpose: To investigate the effects of fatiguing test on the fracture strength of all-ceramic crowns (IPS Empress II, Conventional InCeram and Celay InCeram).

Material and Methods: Twenty crown; shapes 8mm in diameter and 7mm in height were fabricated for each all-ceramic system. For each ceramic system, 10 specimens were tested for fracture strength without fatiguing. A secondly, remaining specimens was submitted to a fatiguing and then fractured using a universal testing machine for each systems. The results were statically analyzed using a one way ANOVA and Student t test.

Results: When comparing the fracture strength of all-ceramic crowns with and without the fatiguing test, the strength was lower after fatiguing (p<0.05). The strength of conventional InCeram specimens was significantly affected after fatiguing test.

Conclusion: These results suggest that although the conventional In Ceram system has high fracture strength, it is more sensitive to fatiguing test within the three all ceramic systems.

ÖZET

Amaç: Yorulma testinin tam seramiklerin (IPS Empress II, Geleneksel InCeram ve Celay InCeram) kırılma direnci üzerine etkisinin araştrılması.

Gereç ve Yöntem: Her seramik sistemi için 8 mm çapında 7 mm yüksekli'inde 20 adet master die hazırlandı. Her seramik sistemi için 10 adet örneğin kırılma direnci yorulma testi uygulanmadan test edildi. İkinci olarak, her gruba ait kalan örneklere yorulma testi uygulandı ve universal test cihazı kullanılarak kırılma testi yapıldı. Elde edilen sonuçlar tek yönlü ANOVA ve student t testi kullanılarak değerlendirildi.

Bulgular: Yorulma testi uygulanan ve uygulanmayan tam seramik kronlar karşılaştırıldığı zaman, yorulma testi sonrası bütün gruplarda kırılma direnci değerleri azaldı (p<0.05). Geleneksel InCeram sistemine ait örnekler yorulma testinden en fazla etkilendi (p<0.05).

Sonuç: Elde edilen sonuçlara göre, üç farklı tam seramik yapım sistemi arasında, geleneksel InCeram sistemi en yüksek kırılma direnci göstermesine rağmen yorulma testinden en fazla etkilenen sistem oldu (p<0.05).

Anahtar kelimeler: Tam seramikler, yorulma testi, vertikal direnç

References

  • Blatz MB. Long-term clinical success of all-ceramic posterior restorations. Quintessence Int 2002; 33: 415-26.
  • McLean JW. Evolution of dental ceramics in the twentieth century. J Prosthet Dent 2001; 85: 61-6.
  • Mclean JW. High-strength ceramics. Quintessence Int 1987;1:97
  • Yoshinari M, Derand T. Fracture strength of all-ceramic crowns. Int J Prosthodont. 1994;7: 329-38.
  • Pröbster L. Survival rate of In-ceram restorations. Int J Prosthodont 1993; 6: 259-63.
  • Yavuzy lmaz H. Metal Destekli Estetik (Veneer – Kaplama) Kronlar. Gazi Üniversitesi Mleti im Fakültesi Bas mevi, Ankara, Özkan P, Yüksel G, Çekiç C. Metal desteksiz porselen sistemleri. Atatürk Üniversitesi Di Hek Fak Derg 2000;10:79-88.
  • White SN, Li ZC, Yu Z, Kipnis V. Relationship between static chemical and cyclic mechanical fatigue in a feldspathic porcelain. Dent Mater 1997; 13:103-10.
  • Sobrinho LC, Cattell MJ, Glover RH, Knowles JC. Investigation of the dry and wet properties of three all-ceramic crown systems. Int J Prosthodont 1998;11: 255-62.
  • Ohyama T, Yoshinari M, Oda Y. Effects of cyclic loading on the strength of all-ceramic materials. Int J Prosthodont 1999;12:28-37.
  • White SN, Caputo AA, Vidjak FM, Seghi RR. Moduli of rupture of layered dental ceramics. Dent Mater 1994;10:52-8.
  • Beschnidt SM, Strub JR. Evaluation of the marginal accuracy of different all-ceramic crown systems after simulation in the artificial mouth. J Oral Rehabil 1999;26 582-93.
  • Strub R, Beschnidt M. Fracture strength of 5 different all-ceramic crown systems. Int J Prosthodont 1998;11:602-9.
  • Campbell SD. Evaluation of the fit and strength of an all-ceramic fixed partial denture. J Prosthet Dent 1988;59;301-6.
  • Bhowmick S, Zhang Y, Lawn BR. Competing fracture modes in brittle materials subject to concentrated cyclic loading in liquid environments: bilayer structures. J Mater Res 2005;20:2792–800.
  • Chai J, Takahashi Y, Sulaiman F, Chong K. Probability of fracture off all-ceramic crowns. Int J Prosthodont 2000;13:420-4.
  • Vult von Steyern P, Ebbesson S, Holmgren J, Haag P, Nilner KJ. Fracture strength of two oxide ceramic crown systems after cyclic pre-loading and thermocycling. J Oral Rehabil 2006;33:682-9.
  • Rinke S, Hüls A, Jahn L. Marjinal accuracy and fracture strength of conventional and copy-milled all-ceramic crowns. Int J Prosthodont 1995;8: 303-10.
  • Aboushelib MN, de Jager N, Kleverlaan CJ, Feilzer AJ. Effect of loading method on the fracture mechanics of two layered all-ceramic restorative systems. Dent Mater 2007;23:952-9.
  • Lee SK, Wilson PR. Fracture strength of all-ceramic crowns with varying core elastic moduli. Aust Dent J 2000;45:103-7.
  • Zahran M, El-Mowafy O, Tam L, Watson PA, Finer YJ. Fracture strength and fatigue resistance of all-ceramic molar crowns manufactured with CAD/CAM technology. J Prosthodont ;17:370-7. Hwang JW, Yang JH. Fracture strength of copy-milled and conventional In-ceram crowns. J Oral Rehabil 2001;28:678-83.
  • Philip GK, Brukl CE. Compressive strengths of conventional, twin foil, and all-ceramic crowns. J Prosthet Dent 1984;52:215-20.
  • Attia A, Kern M. Influence of cyclic loading and luting agents on the fracture load of two all-ceramic crown systems. J Prosthet Dent ;92:551-6. Fischer H, Weiss R, Telle R. Crack healing in alumina bioceramics. Dent Mater 2008;24:328-32.
  • Haselton DR. Clinical assessment of high-strength all-ceramic crowns. J Prosthet Dent 2000; 83:396-401.
  • Gemalmaz D, Ergin S. Clinical evaluation of all-ceramic crowns. J Prosthet Dent 2002;87:189-96. Yaz(Ama Adresi
  • Yrd.Doç.Dr.Mustafa ZORTUK Erciyes Üniversitesi Di Hekimli i Fakültesi Protetik Di Tedavisi Anabilim Dal . Kayseri 38039 Türkiye Tel Faks : 0 352 4380657
  • E-Posta : mzortuk@erciyes.edu.tr

Cumhuriyet Üniversitesi

Year 2009, Volume: 12 Issue: 1, 16 - 21, 01.11.2011

Abstract

Amaç: Yorulma testinin tam seramiklerin (IPS Empress II, Geleneksel InCeram ve Celay InCeram) k r lma direnci üzerine etkisinin ara t r lmas .Gereç ve Yöntem: Her seramik sistemi için 8 mm çap nda 7 mm yüksekli'inde 20 adet master die haz rland . Her seramik sistemi için 10 adet örne'in k r lma direnci yorulma testi uygulanmadan test edildi. .kinci olarak, her gruba ait kalan örneklere yorulma testi uyguland ve universal test cihaz kullan larak k r lma testi yap ld . Elde edilen sonuçlar tek yönlü ANOVA ve student t testi kullan larak de'erlendirildi. Bulgular: Yorulma testi uygulanan ve uygulanmayan tam seramik kronlar kar la t r ld ' zaman, yorulma testi sonras bütün gruplarda k r lma direnci de'erleri azald (p

References

  • Blatz MB. Long-term clinical success of all-ceramic posterior restorations. Quintessence Int 2002; 33: 415-26.
  • McLean JW. Evolution of dental ceramics in the twentieth century. J Prosthet Dent 2001; 85: 61-6.
  • Mclean JW. High-strength ceramics. Quintessence Int 1987;1:97
  • Yoshinari M, Derand T. Fracture strength of all-ceramic crowns. Int J Prosthodont. 1994;7: 329-38.
  • Pröbster L. Survival rate of In-ceram restorations. Int J Prosthodont 1993; 6: 259-63.
  • Yavuzy lmaz H. Metal Destekli Estetik (Veneer – Kaplama) Kronlar. Gazi Üniversitesi Mleti im Fakültesi Bas mevi, Ankara, Özkan P, Yüksel G, Çekiç C. Metal desteksiz porselen sistemleri. Atatürk Üniversitesi Di Hek Fak Derg 2000;10:79-88.
  • White SN, Li ZC, Yu Z, Kipnis V. Relationship between static chemical and cyclic mechanical fatigue in a feldspathic porcelain. Dent Mater 1997; 13:103-10.
  • Sobrinho LC, Cattell MJ, Glover RH, Knowles JC. Investigation of the dry and wet properties of three all-ceramic crown systems. Int J Prosthodont 1998;11: 255-62.
  • Ohyama T, Yoshinari M, Oda Y. Effects of cyclic loading on the strength of all-ceramic materials. Int J Prosthodont 1999;12:28-37.
  • White SN, Caputo AA, Vidjak FM, Seghi RR. Moduli of rupture of layered dental ceramics. Dent Mater 1994;10:52-8.
  • Beschnidt SM, Strub JR. Evaluation of the marginal accuracy of different all-ceramic crown systems after simulation in the artificial mouth. J Oral Rehabil 1999;26 582-93.
  • Strub R, Beschnidt M. Fracture strength of 5 different all-ceramic crown systems. Int J Prosthodont 1998;11:602-9.
  • Campbell SD. Evaluation of the fit and strength of an all-ceramic fixed partial denture. J Prosthet Dent 1988;59;301-6.
  • Bhowmick S, Zhang Y, Lawn BR. Competing fracture modes in brittle materials subject to concentrated cyclic loading in liquid environments: bilayer structures. J Mater Res 2005;20:2792–800.
  • Chai J, Takahashi Y, Sulaiman F, Chong K. Probability of fracture off all-ceramic crowns. Int J Prosthodont 2000;13:420-4.
  • Vult von Steyern P, Ebbesson S, Holmgren J, Haag P, Nilner KJ. Fracture strength of two oxide ceramic crown systems after cyclic pre-loading and thermocycling. J Oral Rehabil 2006;33:682-9.
  • Rinke S, Hüls A, Jahn L. Marjinal accuracy and fracture strength of conventional and copy-milled all-ceramic crowns. Int J Prosthodont 1995;8: 303-10.
  • Aboushelib MN, de Jager N, Kleverlaan CJ, Feilzer AJ. Effect of loading method on the fracture mechanics of two layered all-ceramic restorative systems. Dent Mater 2007;23:952-9.
  • Lee SK, Wilson PR. Fracture strength of all-ceramic crowns with varying core elastic moduli. Aust Dent J 2000;45:103-7.
  • Zahran M, El-Mowafy O, Tam L, Watson PA, Finer YJ. Fracture strength and fatigue resistance of all-ceramic molar crowns manufactured with CAD/CAM technology. J Prosthodont ;17:370-7. Hwang JW, Yang JH. Fracture strength of copy-milled and conventional In-ceram crowns. J Oral Rehabil 2001;28:678-83.
  • Philip GK, Brukl CE. Compressive strengths of conventional, twin foil, and all-ceramic crowns. J Prosthet Dent 1984;52:215-20.
  • Attia A, Kern M. Influence of cyclic loading and luting agents on the fracture load of two all-ceramic crown systems. J Prosthet Dent ;92:551-6. Fischer H, Weiss R, Telle R. Crack healing in alumina bioceramics. Dent Mater 2008;24:328-32.
  • Haselton DR. Clinical assessment of high-strength all-ceramic crowns. J Prosthet Dent 2000; 83:396-401.
  • Gemalmaz D, Ergin S. Clinical evaluation of all-ceramic crowns. J Prosthet Dent 2002;87:189-96. Yaz(Ama Adresi
  • Yrd.Doç.Dr.Mustafa ZORTUK Erciyes Üniversitesi Di Hekimli i Fakültesi Protetik Di Tedavisi Anabilim Dal . Kayseri 38039 Türkiye Tel Faks : 0 352 4380657
  • E-Posta : mzortuk@erciyes.edu.tr
There are 26 citations in total.

Details

Primary Language English
Journal Section Original Research Articles
Authors

Mustafa Zortuk

Sebnem Eskimez

Eylem Ozdemir

Suleyman Aguloglu

Publication Date November 1, 2011
Submission Date November 1, 2011
Published in Issue Year 2009Volume: 12 Issue: 1

Cite

EndNote Zortuk M, Eskimez S, Ozdemir E, Aguloglu S (November 1, 2011) Yorulma testinin, üç farklı tam seramik yapım sistemi vertikal kırılma Direnci üzerine etkisi. Cumhuriyet Dental Journal 12 1 16–21.

Cumhuriyet Dental Journal (Cumhuriyet Dent J, CDJ) is the official publication of Cumhuriyet University Faculty of Dentistry. CDJ is an international journal dedicated to the latest advancement of dentistry. The aim of this journal is to provide a platform for scientists and academicians all over the world to promote, share, and discuss various new issues and developments in different areas of dentistry. First issue of the Journal of Cumhuriyet University Faculty of Dentistry was published in 1998. In 2010, journal's name was changed as Cumhuriyet Dental Journal. Journal’s publication language is English.


CDJ accepts articles in English. Submitting a paper to CDJ is free of charges. In addition, CDJ has not have article processing charges.

Frequency: Four times a year (March, June, September, and December)

IMPORTANT NOTICE

All users of Cumhuriyet Dental Journal should visit to their user's home page through the "https://dergipark.org.tr/tr/user" " or "https://dergipark.org.tr/en/user" links to update their incomplete information shown in blue or yellow warnings and update their e-mail addresses and information to the DergiPark system. Otherwise, the e-mails from the journal will not be seen or fall into the SPAM folder. Please fill in all missing part in the relevant field.

Please visit journal's AUTHOR GUIDELINE to see revised policy and submission rules to be held since 2020.