Purpose: The aim of this study was to investigate microleakage of three different self etching adhesive systems in class II cavities comparatively.
Material and Method: In this study 45 caries free human maxillary premolar teeth were used. Standard class II cavities were prepared on mesial surfaces of all. Teeth were randomly assigned to 3 groups of each 15. Group 1: Prime&Bond NT (Dentsply DeTrey, Konstanz, Germany) + Quixfill (Dentsply DeTrey, Konstanz, Germany), Group 2: Xeno V (Dentsply DeTrey, Konstanz, Germany) + Quixfill, Group 3: G Bond (20) + gradia direct (GC-Fuji Japan). All restorations were applied incrementally according to manufacturers’ recommendations and were polymerized with LED (Elipar Freelight II, 3M-ESPE, Germany). All samples were immersed in distile water for 24hr at 37°C and then were thermocycled at 5° and 55°C for 10000 cycles of 30 seconds each, stained (24 hr) in 0.5% methylene blue, and sectioned mesio-distally following stain development. Microleakage of occlusal and gingival walls were scored from 0 to 4 under stereomicroscope.
Results: In terms of occlusal assessment; statistically there was significance in intergroups (p<0.05). Less microleakage scores were determined in Group 1(Prime&Bond NT). In comparison of Group 2 (Xeno V) and Group 3 (G Bond) there was no significance among occlusal and gingival scores. And statistically no significance was found in gingival scores(p>0.05).
Conclusions: In comparison of applied adhesives; in decreasing gingival and occlusal microleakage, total etch adhesive system (Prime&Bond NT) was found more succesful than the other two self etching adhesive systems (Xeno V, G Bond).
ÖZET
Amaç: Bu çalı manın amacı üç farklı adeziv sistemin (Prime&Bond NT, Xeno V, G Bond) Sınıf II kavitelerdeki mikro sızıntılarının karşılaştırmalı olarak incelemektir.
Gereç ve yöntem: Bu çalışmada çürüksüz 45 adet insan üst çene küçük azı dişi kullanıldı. Dişlerin mezial yüzeylerinde birer adet standart Sınıf II kavite açıldı. Sonra dişler her grupta 15 diş olacak şekilde rastgele 3 gruba ayrıldı. Grup 1: Prime&Bond NT (Dentsply DeTrey, Konstanz, Germany) ve Quixfill (Dentsply DeTrey, Konstanz, Germany), Grup 2: Xeno V (Dentsply DeTrey, Konstanz, Germany) ve Quixfill ile restore edildi, Grup 3: G Bond ve Gradia Direct (GC-Fuji, Tokyo, Japan) uygulandı. Tüm restorasyonlar üretici firmaların önerileri doğrultusunda tabakalama yöntemi ile yerleştirildi ve LED (Elipar Freelight II,3M-ESPE, Germany) ışık kaynağı kullanılarak polimerize edildi. Örnekler etüvde 370C de 24 saat distile su içerisinde bekletildi. 30 saniye kalacak şekilde 5 ve 55°C termal siklus işlemi 10000 kez uygulandı. Bütün dişler 24 saat % 0.5’lik metilen mavisi içerisinde bekletildi. Dişler mesio-distal yönde kesildi, stereo mikroskop altında oklüzal ve gingival duvarlar 0 ile 4 arasındaki skorlar ile değerlendirildi. Elde edilen veriler Kruskal Wallis ve Mann Whitney testleri ile değerlendirildi.
Bulgular: Oklüzal mikro sızıntının değerlendirilmesinde gruplar arasında istatistiksel anlamlılık bulundu (P<0.05). Grup 1 (Prime&Bond NT) de daha düşük mikro sızıntı skorları tespit edildi. Grup 2 (Xeno V) ve Grup 3 (G Bond) birbirleriyle kıyaslandığında oklüzal ve gingival değerler arasında farklılık bulunmadı (p>0.05). Gingival de ise üç grup arasında istatistiksel anlamlılık bulunmadı (p>0.05).
Sonuç: Uygulanan adezivlerin karşılaştırılmasında; oklüzal ve gingival de total etch (Prime&Bond NT) adeziv sistem mikro sızıntıyı azaltmada diğer iki self etching (Xeno V, G Bond) adeziv sistemden daha başarılı bulunmuştur.
Amaç: Bu çal man n amac üç farkl adeziv sistemin (Prime&Bond NT, Xeno V, G Bond) S n f II kavitelerdeki mikro s z nt lar n nkar la t rmal olarak incelemektir. Gereç ve yöntem: Bu çal mada çürüksüz 45 adet insan üst çene küçük az di i kullan ld . Di lerin mezial yüzeylerinde birer adet standart S n f II kavite aç ld . Sonra di ler her grupta 15 di olacak ekilde rastgele 3 gruba ayr ld . Grup 1: Prime&Bond NT (Dentsply DeTrey, Konstanz, Germany) ve Quixfill (Dentsply DeTrey, Konstanz, Germany), Grup 2: Xeno V (Dentsply DeTrey, Konstanz, Germany) ve Quixfill ile restore edildi, Grup 3: G Bond ve Gradia Direct (GC-Fuji, Tokyo, Japan) uyguland . Tüm restorasyonlar üretici firmalar n önerileri do:rultusunda tabakalama yöntemi ile yerle tirildi ve LED (Elipar Freelight II,3M-ESPE, Germany) kkayna: kullan larak polimerize edildi. Örnekler etüvde 37oC de 24 saat distile su içerisinde bekletildi. 30 saniye kalacak ekilde 5 ve 55°C termal siklus i lemi 10000 kez uyguland . Bütün di ler 24 saat % 0.5’lik metilen mavisi içerisinde bekletildi. Di ler mesio-distal yönde kesildi, stereo mikroskop alt nda oklüzal ve gingival duvarlar 0 ile 4 aras ndaki skorlar ile de:erlendirildi. Elde edilen veriler Kruskal Wallis ve Mann Whitney testleri ile de:erlendirildi. Bulgular: Oklüzal mikro s z nt n n de:erlendirilmesinde gruplar aras nda istatistiksel anlaml l k bulundu (P0.05). Gingival de ise üç grup aras nda istatistiksel anlaml l k bulunmad (p>0.05). Sonuç: Uygulanan adezivlerin kar la t r lmas nda; oklüzal ve gingival de total etch (Prime&Bond NT) adeziv sistem mikro s z nt yazaltmada di:er iki self etching (Xeno V, G Bond) adeziv sistemden daha ba ar l bulunmu tur
Primary Language | English |
---|---|
Journal Section | Original Research Articles |
Authors | |
Publication Date | October 30, 2011 |
Submission Date | October 30, 2011 |
Published in Issue | Year 2009Volume: 12 Issue: 2 |
Cumhuriyet Dental Journal (Cumhuriyet Dent J, CDJ) is the official publication of Cumhuriyet University Faculty of Dentistry. CDJ is an international journal dedicated to the latest advancement of dentistry. The aim of this journal is to provide a platform for scientists and academicians all over the world to promote, share, and discuss various new issues and developments in different areas of dentistry. First issue of the Journal of Cumhuriyet University Faculty of Dentistry was published in 1998. In 2010, journal's name was changed as Cumhuriyet Dental Journal. Journal’s publication language is English.
CDJ accepts articles in English. Submitting a paper to CDJ is free of charges. In addition, CDJ has not have article processing charges.
Frequency: Four times a year (March, June, September, and December)
IMPORTANT NOTICE
All users of Cumhuriyet Dental Journal should visit to their user's home page through the "https://dergipark.org.tr/tr/user" " or "https://dergipark.org.tr/en/user" links to update their incomplete information shown in blue or yellow warnings and update their e-mail addresses and information to the DergiPark system. Otherwise, the e-mails from the journal will not be seen or fall into the SPAM folder. Please fill in all missing part in the relevant field.
Please visit journal's AUTHOR GUIDELINE to see revised policy and submission rules to be held since 2020.